The surface structure and the fatigue fracture specifications of steel samples ( ) with stress concentrators are considered, which are modelling thread helix on the working surface of shafts. For carrying out technical diagnostics of fracture causes resulted from microhardness measurements of surface layers of fractures the systems of regression equations are obtained, which can be used for recovering the cyclic overstrain and the fatigue life that cause fracture.